Abstract
AbstractThe effects of Baltic seawater on frost durability of PC concretes using sulfate resistant portland cement and combination of rapid hardening portland cement with silica fume were studied. The freeze-thaw cycles were performed on specimens exposed to the Baltic seawater, 3% sodium chloride solution and deionized water. The freeze-thaw cycles appeared to cause the most extensive internal damage in specimens based on sulfate resistant cement (SR) and exposed to seawater. The most extensive surface scaling was observed in the case of concretes containing silica fume and exposed to deicing salts. Based on the thermo gravimetric and X-ray diffraction analyses it was concluded that extensive internal damage of concrete based on SR was caused by changes of the microstructure due to secondary formation of ettringite, carbonation, and formation of calcite. The results showed also that low C3A content of the SR did not fully mitigate formation of secondary ettringite during freeze-thaw cycles. A combination...
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.