Abstract
The phosphor powders with the composition of Ba 1.1Sr 0.88SiO 4:Eu 0.02 were prepared by spray pyrolysis. Barium fluoride and barium nitrate were used as the source materials of Ba component. Ba 1.1Sr 0.88SiO 4:Eu 0.02 phosphor powders had broad excitation wavelength ranging from 220 to 460 nm irrespective of mole ratios of barium fluoride and barium nitrate. Ba 1.1Sr 0.88SiO 4:Eu 0.02 phosphor powders had broad emission spectrum between 470 and 600 nm and had the maximum peak intensity at 522 nm. Substitution of BaF 2 instead of some amount of barium nitrate improved the photoluminescence intensities of Ba 1.1Sr 0.88SiO 4:Eu 0.02 phosphor powders. The maximum photoluminescence intensity of Ba 1.1Sr 0.88SiO 4:Eu 0.02 phosphor powders prepared from spray solution with barium fluoride and barium nitrate was about 595% of the phosphor powders prepared from spray solution without barium fluoride. The sky blue light emitting LED with prepared phosphor powders showed (0.1958 and 0.2719) on the CIE chromaticity diagram and luminous intensity of 1.68 cd.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.