Abstract
Phosphate glasses having composition, 40Na2O-10BaO-xB2O3-(50-x)P2O5, wherex = 0–20 mol% were prepared using conventional melt quench technique. Density of these glasses was measured using Archimedes principle. Microhardness (MH) was measured by Vicker’s indentation technique. Structural studies were carried out using IR spectroscopy and31P and11B MAS NMR. Density was found to vary between 2.62 and 2.77 g/cc. MH was found to increase with the increase in boron content.31P MAS NMR spectra showed the presence of middle Q2 groups and end Q1 and Q0 groups with P-O-B linkages. FTIR studies showed the presence of BO3 and BO4 structural units along with the depolymerization of phosphate chains in conformity with31P MAS NMR.11B NMR spectra showed increase in BO4 structural units with increasing boron content. The increase in MH with B2O3 content is due to the increase of P-O-B linkages and BO4 structural units as observed from MAS NMR studies resulting in a more rigid borophosphate glass networks.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.