Thin films of ZrSe 2 have been prepared on stainless steel and fluorine-doped tin oxide-coated glass substrates using electrodeposition technique at potentiostatic mode. Double-distilled water containing precursors Zr and Se with ethylene diamine tetra-acetic acid disodium salt as a complexing agent was used to obtain good quality deposits by controlling the rate of reaction. The preparative parameters such as concentration of bath, deposition time, bath temperature, pH of the bath and annealing temperature have been optimized using photoelectrochemical (PEC) technique. The films deposited at optimum preparative parameters are annealed at different temperatures. The film annealed at 200 °C shows more photosensitivity. The as-deposited and annealed films at 200 °C have been characterized by X-ray diffraction (XRD), energy dispersive analysis by X-ray (EDAX), optical absorption and scanning electron microscopy (SEM). The XRD analysis of the as-deposited and annealed films showed the presence of polycrystalline nature with hexagonal crystal structure. EDAX study reveals that deposited films are almost stoichiometric. Optical absorption study shows the presence of direct transition and band gap energies are found to be 1.5 and 1.38 eV, respectively, for the as-deposited and annealed films. SEM study revels that the grains are uniformly distributed over the surface of substrate for the as-deposited as well as annealed film, which indicates formation of good and compact type of crystal structure.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.