Abstract
Zinc oxide nanofibers doped with aluminum oxide were prepared by sol–gel processing and electrospinning techniques using polyvinylpyrrolidone (PVP), zinc acetate and aluminum acetate as precursors. The resulting nanofibers were characterized by scanning electron microscopy (SEM), X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), UV–Vis spectroscopy, and current–voltage ( I– V) properties. The nanofibers had diameters in the range of 60–150 nm. The incorporation of aluminum oxide resulted in a decrease in the crystallite sizes of the zinc oxide nanofibers. Aluminum oxide doped zinc oxide (AOZO) nanofibers exhibited lower bandgap energies compared to undoped zinc oxide nanofibers. However, as the aluminum content (Al/(Al + Zn) × 100%) was increased from 1.70 at.% to 3.20 at.% in the electrospinning solution, the bandgap energy increased resulting in lower conductivity. The electrical conductivity of the AOZO samples was found to depend on the amount of aluminum dopant in the matrix as reflected in the changes in oxidation state elucidated from XPS data. Electrospinning was found to be a productive, simple, and easy method for tuning the bandgap energy and conductivity of zinc oxide semiconducting nanofibers.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.