ABSTRACTThe effect of adhesive thickness on stringiness behavior during 90° peel testing was investigated for crosslinked poly(n‐butyl acrylate‐acrylic acid) (A) and poly(2‐ethylhexyl acrylate‐acrylic acid) (B) with a constant crosslinker content. The adhesive thickness was varied over the range from 15 to 60 μm. All adhesive thicknesses exhibited sawtooth‐type peeling with a front frame for B, but only the 30‐μm thickness generated a front frame‐type for A. The peel rate decreased from 15 to 45 μm and plateaued above 45 μm under a constant load test. These results indicate that the adhesion strength increases with adhesive thickness, but reaches a constant value at high thicknesses. The stringiness was also analysed for B and the sawtooth interval observed to increase with increasing thickness. This means the sawtooth number decreased. As a result, the concentrated stress per sawtooth induces easier peeling and so this factor tend to increase the peel rate. Conversely, the stringiness width increased with increasing thickness. The stress load over the stringiness region decreased with an increase in thickness, meaning that a decrease in the concentrated stress decreases the peel rate. The actual peel rate is influenced by the contributions of these two factors. The strain rates during constant peel rate tests decreased slightly with increasing thickness, due to a reduction in the apparent modulus. The molecular mobilities near the adherend and the backing surfaces were evidently restrained by these surfaces, and the relative rates of motion of such restrained molecules decrease with increased thickness. © 2015 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2015, 132, 42210.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.