Abstract
Objective This study aimed to evaluate the effect of accelerated aging on the sorption and solubility percentages of the MDX4-4210 and A-2186 silicones. Materials and Methods Two silicones (A-2186 and MDX4-4210) and three intrinsic pigments (bronze, black, and pink) were used in this study. Thus, six groups were created ( n = 10): Group 1 = bronze MDX4-4210; Group 2 = black MDX4-4210; Group 3 = pink MDX4-4210; Group 4 = bronze A-2186; Group 5 = black A-2186; and Group 6 = pink A-2186. The dimensions of all samples were the same (45-mm diameter (ø) × 1-mm thickness). The samples were aged for a total of 1,008 hours. In this period of 1,008 hours of accelerated aging, the sorption and solubility percentages of each sample were calculated at three time points (252, 504, and 1,008 hours). Statistical Analysis Three-way analysis of variance (ANOVA) and the Tukey test were performed (α = 0.05). Result Accelerated aging can significantly increase the sorption and solubility percentages of the MDX4-4210 and A-2186 silicones.
Highlights
Congenital defects, trauma, or cancer can often cause facial tissue disfigurement, leading to distress, few job opportunities, bullying, and discrimination for people with this problem.[1]
This study aimed to evaluate the effect of accelerated aging on the sorption and solubility percentages of the MDX4-4210 and A-2186 silicones
The samples were aged for a total of 1,008 hours. In this period of 1,008 hours of accelerated aging, the sorption and solubility percentages of each sample were calculated at three time points (252, 504, and 1,008 hours)
Summary
This study aimed to evaluate the effect of accelerated aging on the sorption and solubility percentages of the MDX4-4210 and A-2186 silicones. Materials and Methods Two silicones (A-2186 and MDX4-4210) and three intrinsic pigments (bronze, black, and pink) were used in this study. The dimensions of all samples were the same (45-mm diameter (ø) × 1-mm thickness). The samples were aged for a total of 1,008 hours. In this period of 1,008 hours of accelerated aging, the sorption and solubility percentages of each sample were calculated at three time points (252, 504, and 1,008 hours). Result Accelerated aging can significantly increase the sorption and solubility percentages of the MDX4-4210 and A-2186 silicones
Sign-in/Register to view highlights & summary 
Published Version (
Free)
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a call