Abstract
The effect of α2 precipitation on the creep and tensile properties was investigated for bimodal and lamellar microstructures in two Ga-added near-α Ti alloys with Al equivalences of 10.6 and 11.5. Fine α2 phase formed in the α phase of both alloys. The volume fraction of the α2 phase for the Al equivalences of 10.6 and 11.5 is equivalent to 57.6 % and 73.3 %, respectively, in the binary Ti-Al system at 600 °C. Creep tests were carried out under a constant stress of 310 MPa at 600 °C and tensile tests were performed at room temperature. Lamellar microstructure showed lower minimum creep strain rates than bimodal microstructure for both alloys. The increase in Al equivalence increased creep life by a factor of 1.6 and decreased the minimum creep strain rate from 6.51 × 10-8 s-1 to 3.99 × 10-8 s-1 in bimodal microstructure. In addition, the increase in Al equivalence decreased room temperature tensile elongation although both alloys contained a similar volume fraction of equiaxed α in a bimodal microstructure.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.