Abstract
The broadband dielectric spectroscopy was carried out in the frequency range of 1–107 Hz at the −20–200°C range to investigate the effect of temperature on the dynamic thermal–dielectric behavior of the aluminum (Al)/epoxy composite. The epoxy composites with core-shell–structured Al particles were prepared by solution method. The results show that the dielectric permittivity of the composites increased smoothly with a rise of filler content and reduced with an increase in frequency at room temperature. While the dielectric loss and conductivity still remained at low level owing to the nanoscale alumina insulating shell serving as a barrier layer to control the dielectric loss. The dielectric permittivity, dissipation factor, and conductivity of the composites increased with temperature and exhibited an abrupt rise around the glass transition temperature ( Tg). A large increase in the dissipation factor and conductivity with temperature is attributed to the direct current conduction of thermal-activated charge carriers resulting from pure epoxy above Tg. The observed temperature-dependent dielectric relaxations of the composites indicated a thermally activated behavior of the relaxation time of epoxy chain segments.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.