Durability of self-healing dental composites: A comparison of performance under monotonic and cyclic loading

Abstract

Durability is an important quality of dental restorative materials, and the ability to autonomously heal damage incurred during their oral function is highly desirable. ObjectiveThe objective was to evaluate the improvement in durability of self-healing dental composites (SHDCs) in terms of their resistance to fracture and capacity for healing of damage under monotonic and cyclic loading. MethodsSHDCs were prepared by incorporating dental resin composites with microcapsules containing healing liquid. Control specimens with the same mass fraction (5% and 25%) of microcapsules filled with water were also evaluated. Two sets of SHDCs were distinguished by the silane coupling agents that functionalized and bonded the microcapsules to resin network. One set used a methacrylate silane (MA-silane) that connected resin network through covalent bonds, and the other used a H-bonding forming hydroxyl silane (OH-silane). The fatigue crack growth resistance was assessed in terms of the threshold stress intensity range and the conventional Paris Law parameters. Cyclic loading was conducted at 5 Hz with maximum cyclic load ranged between approximately 1 N and 5 N. The efficiency of the autonomous healing was determined per the recovering of the fracture toughness and the extension of fatigue life. ResultsThe SHDCs with 5 wt% of healing microcapsules exhibited a larger fracture toughness than those with 25 wt% microcapsules. MA-silane SHDCs had approximately five times more responsive microcapsules triggered by fracturing of the composites. Consequently, the MA-silane SHDCs with 5 wt% of microcapsules achieved the best performance in terms of fracture toughness and healing efficiency. In regards to the fatigue crack growth behavior, there was a significant increase in the resistance to fatigue crack growth and 580 ± 15% improvement in the fatigue life. SignificanceStrong silanization is vital in SHDCs to simultaneously achieve clinically applicable mechanical performance and substantial healing capability. Moreover, the evaluation of self-healing under cyclic loading is a promising tool in quantifying the degree of fracture-induced healing.