Dry sliding wear behavior of AA7075 alloy produced by thixocasting

Abstract

Abstract In this study, the wear behavior of AA7075 alloy produced by thixocasting was investigated. The wear behavior of the AA7075 alloy is examined for three cases: extruded with T6 heat treatment, as-thixocast, and thixocast with T6 conditions. The dry sliding wear test was conducted with a tribometer according to ASTM G-99 standard. The microstructures were characterized by optical microscopy, scanning electron microscopy (SEM), and energy-dispersive X-ray analysis (EDX). The tensile and hardness tests were performed to evaluate the mechanical properties. The AA7075 alloy was successfully shaped by thixocasting. The as-thixocast sample exhibited typical globular structures with multinary eutectic structures along the grain boundaries. The globular grains transform into a polygonal structure, and the grain size increases from 50 μm to 60 μm in the thixocast + T6 sample. This microstructure exhibited excellent wear resistance under dry sliding conditions in the thixocast + T6 sample. The aging treatment with prolonged solution process improved the mechanical properties two times and the wear rate three times for the thixocast AA7075 alloy. Furthermore, the thixocast + T6 sample exhibited a significant decrease in the coefficient of friction with the lowest wear rate compared to the as-thixocast sample. The dominant wear mechanisms are microdelamination, adhesion, and oxidation in all samples.