Abstract
Different doses of γ-radiation can be used to modify the structural and magnetic properties of a host of materials. The Mn0.5Zn0.5Fe2O4 ceramics samples prepared by the solution combustion route were exposed to different doses of γ-radiation in order to study stability and phase transformations. The creation of defects and building up of strain was observed after medium doses of γ-irradiation (up to 25kGy) into the single phase pristine samples. However, after 50kGy of γ-irradiation the locally generated heat drives atomic diffusion, as indicated by the morphological changes in the sample. Furthermore, the sample decomposed into two new stable crystalline phases, α-Fe2O3 and ZnFe2O4, along with amorphous MnO phase. Besides the structural transformations we have observed the deterioration of magnetic properties at higher doses. Our results are important for understanding the stability and performance of the ferrite based devices used near intense high energy radiation sources.
Sign-in/Register to access full text options 
Free) 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a call