Abstract
The primary creep behavior at ambient temperature of typical h.c.p., b.c.c. and f.c.c. metals and alloys of annealed state was surveyed and the deformation mechanism of CP-Ti was discussed through transmission electron microscopy. Only h.c.p. metals and alloys demonstrated significant creep at ambient temperature. Arrays of straight screw dislocations of b=1/2<2110> and <2110> direction were observed in the crept CP-Ti.