Abstract
AbstractHerein, cellulose nanofibers (PO‐CNFs) and cellulose nanocrystals (PO‐CNCs) are prepared directly from native softwood spruce and hardwood beech via the same alkaline periodate oxidation under equal conditions. PO‐CNFs and PO‐CNCs are obtained by simply regulating the reaction time between 2 and 7 d. Of particular note, the preparation of CNFs is achieved using the alkaline periodate oxidation. PO‐CNFs obtained from spruce and beech have average diameters of 7.2 ± 3.1 and 6.8 ± 3.0 nm as well as average lengths of 487.1 ± 69.0 and 452.1 ± 80.0 nm, respectively. The PO‐CNCs obtained from spruce and beech are 4.6 ± 2.0 and 4.8 ± 2.5 nm in diameter as well as 181.6 ± 49.4 and 168.4 ± 59.0 nm in length, respectively. These nanocelluloses contain carboxy groups that enable good colloidal stability of nanocelluloses in water. The nanocellulose content isolated from spruce and beech increase with the reaction time and reach 1.35 ± 0.20 and 1.24 ± 0.10 mmol g–1 after oxidation for 7 d, respectively. Both PO‐CNFs and PO‐CNCs can be used for the formation of highly transparent films with good mechanical properties.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.