Abstract
The fabrication of patterned polymer brushes has attracted considerable attention as these structures can be exploited in devices on the nano- and microscale. Patterning of polymer brushes is typically a complex, multistep process. We report the direct patterning of poly(methyl methacrylate) (PMMA), poly(2-hydroxyethyl methacrylate) (PHEMA), poly(isobutyl methacrylate) (PIBMA), poly(neopentyl methacrylate) (PNPMA), and poly(2,2,2-trifluoroethyl methacrylate) (PTFEMA) brushes in a single step by electron beam (e-beam) lithography, to obtain nanopatterned polymer brush surfaces. PMMA, PHEMA, PIBMA, PNPMA, and PTFEMA brushes were grown on silicon substrates via surface-initiated atom transfer radical polymerization. Surface analysis techniques including ellipsometry, contact angle goniometry, atomic force microscopy (AFM), and X-ray photoelectron spectroscopy (XPS) were used to characterize the thickness, hydrophilicity, roughness, and chemical composition of the polymer brushes. Tapping-mode AFM imaging confirmed the successful electron beam patterning of these brushes. Using this direct patterning method, highly resolved nanostructured polymer brush patterns down to 50 nm lines were obtained. This direct patterning of brushes eliminates the need for complex lithographic schemes. The sensitivity of these polymer brushes toward direct patterning with e-beam was studied and compared. The sensitivity curves indicate that the structure of the e-beam degradable methacrylate polymer has a significant effect on the sensitivity of the polymer brush toward e-beam patterning. In particular, the effect of the chemical functionality at the beta-position to the carbonyl group on the polymer brush sensitivity toward direct patterning was studied using groups of varying size and polarity.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.