Abstract
The origin of ultralow friction and high wear resistance in ultrananocrystalline diamond (UNCD) films is still under active debate because of the perplexed tribochemistry at the sliding interface. Herein, we report a comparative study on surface topography and nanoscale friction of tribofilms, in wear tracks of two sets of UNCD films having different structural characteristics. Despite both the films display ultralow coefficient of friction, the UNCD films grown under Ar atmosphere (UNCDAr) exhibit a high wear resistance while the wear rate is higher for the films grown in N2 (UNCDN). Frictional force microscopic (FFM) investigations clearly reveal the manifestation of shear induced graphitization on both the films. However, the wear track of UNCDAr films have a large network of a few layer graphene (FLG) structures over the amorphous carbon tribofilms while only isolated clusters of FLG structures are present in the wear track of UNCDN films. Here, we demonstrate the direct micro-/nanoscopic evidence for the formation of large network of ~ 0.8 - 6 nm thick FLG structures, as a consequence of shear induced graphitization and discuss their decisive role in ultralow friction and wear.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.