Abstract
Hexaferrites that exhibit the intrinsic and strong magnetoelectric (ME) coupling effect have been considered the most promising candidate for single-phase multiferroics. Currently, the strong ME coupling effect in this system was widely reported in single crystal form, while it is rare in polycrystalline one. In this work, Y-type hexaferrite BaSrCo2Fe12-xAlxO22 (x = 0.0, 0.3, 0.6 and 0.9) ceramics were manufactured with conventional solid-state reaction. Their magnetic, dielectric, and ME coupling properties were systematically surveyed. It was revealed that Al doping could result in a high magnetic transition temperature of ~ 345 K for x = 0.9. Also, the ferroelectric polarization and abnormal magnetodielectric properties were significantly enhanced which could be maintained down to 200 K. Most interestingly, the sample x = 0.9 displayed strong direct and converse ME coefficients of ~ 400 ps/m and ~ 900 ps/m at 150 K, respectively. Therefore, these results reveal that Al doping can broaden our understanding of the Y-type hexaferrite in room-temperature multiferroics.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.