Abstract
By means of Rutherford backscattering spectrometry, electron microscopy, and energy-dispersive X-ray spectroscopy, the distribution and interaction of In and As atoms implanted into thermally grown SiO2 films to concentrations of about 1.5 at % are studied in relation to the temperature of subsequent annealing in nitrogen vapors in the range of T = 800–1100°C. It is found that annealing at T = 800–900°C results in the segregation of As atoms at a depth corresponding to the As+-ion range and in the formation of As nanoclusters that serve as sinks for In atoms. An increase in the annealing temperature to 1100°C yields the segregation of In atoms at the surface of SiO2 with the simultaneous enhanced diffusion of As atoms. The corresponding diffusion coefficient is DAs = 3.2 × 10–14 cm2 s–1.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.