Abstract
(1−x) Pb [ Yb 1/2 Nb 1/2 ] O 3 –x PbTiO 3 (PYbN–PT, x=0.5) epitaxial thin films were deposited on (001) SrRuO3/(001) MgO substrates by sol-gel processing. X-ray diffraction analysis revealed that the films were pyrochlore-free (001) epitaxial films when crystallized at 750 °C for 1 min. The dielectric permittivity and loss factor varied only slightly with frequency in the range of 100 to 10 000 Hz. At 1 kHz, the dielectric permittivity was 870 and the dielectric loss was 0.03 at room temperature. Compared with (111) PYbN–PT films, (001) PYbN–PT films exhibited better ferroelectric and piezoelectric properties. The remanent polarization (Pr) was 37 μC/cm2. The effective transverse piezoelectric e31,f coefficient of the films were −10.2 C/m2 when films were poled at room temperature. Enhanced piezoelectric properties were obtained using unique two-step method poling the PYbN–PT films at higher temperatures.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.