Dielectric and piezoelectric properties of lead-free 0.5Ba(Zr0.2 Ti0.8)O3-0.5(Ba0.7Ca0.3)TiO3 piezoelectric ceramics with glass additive.

Abstract

We have investigated the dielectric and piezoelectric properties of lead-free 0.5Ba(Zr0.2Ti0.8)O3-0.5(Ba0.7Ca0.3)TiO3 ceramics with BaO-CaO-SiO2 glass additive as a function of sintering temperatures. With adding BaO-CaO-SiO2 glass additive, diffusivity of lead-free 0.5Ba(Zr0.2Ti0.8)O3-0.5(Ba0.7Ca0.3)TiO3 ceramics was increased. The dispersion constant γ of BZT-BCT ceramics with BaO-CaO-SiO2 glass was changed from 1.9683 to 1.7673 by decreasing sintering temperature ranging from 1450 degrees C to 1350 degrees C, while 0.5Ba(Zr0.2Ti0.8)O3-0.5(Ba0.7Ca0.3)TiO3 ceramics at sintered 1450 degrees C showed γ = 1.5055. The piezoelectric properties such as electromechanical coupling factor (k(p)) and piezoelectric constant (d33) of lead-free 0.5Ba(Zr0.2Ti0.8)O3-0.5(Ba0.7Ca0.3)TiO3 ceramics with BaO-CaO-SiO2 glass additive sintered at 1400 degrees C showed similar values compared with 0.5Ba(Zr0.2Ti0.8)O3-0.5(Ba0.7Ca0.3)TiO3 ceramics without BaO-CaO-SiO2 glass additive sintered at 1450 degrees C. The addition of BaO-CaO-SiO2 glass additive can be of help to decrease sintering temperature of lead-free 0.5Ba(Zr0.2Ti0.8)O3-0.5(Ba0.7Ca0.3)TiO3 ceramics.