Abstract
Pyrolysis of thermally thick beech wood blocks with a size of around 2.5 × 8 × 6 cm3 (width × length × height) was carried out in a lab scale microwave reactor with a frequency of 2.45 GHz, operated, both, at 300 W and 600 W under inert conditions, using N2 at around 400 mbar absolute pressure. The microwave cavity had a size of 20 × 20 × 20 cm3. The specific energy supply referred to the untreated wood block was 4–8 W/g, with slight variations depending on the initial water content. The mass loss and the reflected microwave power were in-situ monitored during the experiments. The sample surface and chamber temperatures were measured with a pyrometer and a thermocouple, respectively. Physico-chemical and dielectric properties of the produced solids were investigated and compared to those of chars produced under conventional pyrolysis using the same raw materials. It is shown that the complex dielectric permittivity of the solid products changed drastically during the pyrolysis process, with increasing heating properties as the conversion process evolved. This was easily achieved using 600 W without susceptors. However, 300 W was not enough to achieve a high conversion degree, independently of the irradiation time. This, together with the physico-chemical analyses of the solids, hinted to the importance of the transport kinetics in thermally thick materials, although further investigation is still required.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.