Development of the Process of Pseudo-Ligatures Manufacturing from Aluminum and Nickel Powders for the Modification of Alloys

Abstract

Compacting after pressing and sintering of briquettes made from an aluminum powder with an average particle size from 50 to 150 microns, the specific surface area Ssp=0.26 m2/g and a nickel powder with an average particle size from 25 to 100 microns, the specific surface area Ssp= 0.03 m2/g has been investigated. Pressing load varied from 15 to 25 MPa for the aluminum powder and from 20 to 45 MPa for the nickel powder. Sintering of aluminum powder briquettes was carried out at temperatures (0.5-0.83) of melting temperature, (0.3-0.46) of melting temperature from the nickel powder. It is shown that the application of high pressure, low temperatures and short time makes it possible to receive pseudo-ligatures from an aluminum powder with porosity about 32% and a nickel powder with porosity about 30%.