Abstract
Gadolinia-doped ceria (GDC) and lanthanum silicate (LS) are expected to be promising materials for electrolytes of solid oxide fuel cells (SOFCs) because of their high ionic conductivities at intermediate temperatures. However, performance degradation of SOFCs is caused by current leakage through GDC and poor densification of LS. In the present study, LS was used as a blocking layer for preventing the current leakage of GDC electrolyte. Thermal shrinkage measurements and scanning electron microscopy (SEM) observation suggested that the addition of Bi2O3 in LS electrolyte (LSB) contributed to the decrease in the sintering temperature of the LS and improved densification of the GDC/LS bi-layer electrolyte. Consequently, the open-circuit voltage for the cell with GDC/LS and GDC/LSB bi-layer electrolytes increased effectively in comparison with that of the cell with GDC single-layer electrolyte. The electrical conductivity and fuel cell characteristics were compared among the cells with GDC, GDC/LS, and GDC/LSB electrolytes.
Published Version
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a call