Abstract
Tanks made of three different brands of rotational polyethylene (DOW, ELTEX, and M350) with three degrees of sintering (normal sintering (NS), incomplete sintering (ICS), and thermally degraded sintering (TDS)) and three thicknesses (7.5 mm, 8.5 mm, and 9.5 mm) were explored. It was found that the thickness of the walls of the tanks did not have a statistically significant effect on the parameters of the ultrasonic signal (USS). An increase in temperature caused a decrease in the USS parameters. According to the temperature coefficient of stability, the ELTEX brand of plastic can be distinguished (from DOW and M350). The ICS degree of the sintering of the tanks was revealed from a significantly lower amplitude of the bottom signal, compared with NS and TDS degree samples. By analyzing the amplitude of the third harmonic of the ultrasonic signal (β), three degrees of the sintering of containers NS, ICS, and TDS were revealed (with an accuracy of about 95%). Equations β = f(T, PIAT) were derived for each brand of rotational polyethylene (PE), and two-factor nomograms were constructed. Based on the results of this research, a method for the ultrasonic quality control of polyethylene tanks manufactured using rotational molding was developed.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.