Abstract
Sol–gel alumina coatings were deposited on medical grade stainless steel (AISI 316L) with an intermediate layer of silica by dip-coating method. The coatings obtained were homogeneous, crack-free and consisted of low crystalline γ-Al 2O 3 along with some boehmite phase. EDAX revealed the presence of only Al in the film. The corrosion performance of alumina-coated stainless steel was evaluated by electrochemical polarization, open-circuit potential measurement and chronoamperometry in Ringer's solution. Coating has shown to enhance the pitting potential of AISI 316L by ∼ 470 mV and reduced passive current ≤ 10 − 9 A cm − 2 . The formation of thermodynamically stable silica–alumina interface was proposed to account for enhanced corrosion protection behaviour of the coating.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.