Abstract
The corrosion behavior of Zircaloy-4 (Zry-4), specifically by oxidation, is a problem of great importance as this material is critical for current nuclear reactor cladding. The early formation behavior and structure of the oxide layer during oxidation was studied using in-situ TEM techniques that allowed for Zry-4 to be monitored during corrosion. These environmental exposure experiments were coupled with precession electron diffraction to identify and quantify the phases present in the samples before and after the oxidation. Following short-term, high temperature oxidation, the dominant phase was revealed to be monoclinic ZrO2 in a columnar structure. These samples oxidized in-situ contained structures that correlated well with bulk Zry-4 subjected to autoclave treatment, which were used for comparison and validation of this technique. By using in-situ TEM the effect of microstructure features, such as grain boundaries, on oxidation behavior of an alloy can be studied. The technique presented herein holds the potential to be applied any alloy system to study these effects.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.