Deposition of NiAl/Al3Ni2(CrB2) Coatings from Ni, Al and CrB2 Powders Using Mechanical Synthesis in Planetary Ball Mill.

Abstract

Interest in composite thick coatings with an intermetallic matrix stimulates the development of new deposition techniques like the co-milling of pre-alloyed NiAl powder with platelet-shaped substrates. Obtained coatings were up to several micrometers thick as cold-welding of intermetallic particles was effective only at the start of this process, while later, chipping prevailed over added material. The present experiment covered the co-milling in the planetary ball mill of Ni and Al elemental powders (1:1 molar ratio) with AISI 304 steel platelets for 32 h at 300 rpm. Next, this process was repeated with an admixture of 15 wt.% of CrB2 powder. In both cases, their milling succeeded in producing up to a 200 μm coating after 4 h. The use of light, scanning and transmission electron microscopy (LM/SEM/TEM) helped to establish that the coatings had gradient microstructures with more refined crystallites of NiAl, Al3Ni2 and CrB2 closer to the surface. With the addition of a ceramic phase, the coatings presented higher hardness and lower friction during dry wear tests both at RT and at 500 °C.