Abstract
ZrO2 thin films were deposited at 1 atm on Si substrates by oxidation-assisted thermal decomposition of zirconium-trifluoroacetylacetonate in the temperature range of 300–615 °C. Above a deposition temperature of 400 °C, the deposited thin films have a columnar grain structure, where each grain is perpendicular to the substrate surface with a c-axis preferred crystallographic orientation, and have poor electrical characteristics as a dielectric thin film. But the thin film deposited at 350 °C has a fine equiaxed microcrystalline structure and has superior electrical characteristics of a breakdown field of 1 MV/cm and a relative dielectric constant of 27.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.