Abstract
Perovskite LaCoO3 nanopowders were synthesized via solution auto-combustion chemical route, using lanthanum and cobalt nitrates as oxidants and citric acid as fuel. Qualitative and Quantitative phase analysis performed by Rietveld refinements indicated the presence of pure single LaCoO3 phase. From fit parameters, goodness of fit “S” parameter (close to 1) and the difference between the experimental and theoretical XRD patterns. FTIR spectra showed two characteristics bands at 408 and 589 cm−1 characteristics of metal oxygen bands vibration, thus confirming the formation of LaCoO3 phase, whereas the strong absorption band at 589 cm−1 was assigned to Co–O stretching vibration and O–Co–O deformation modes of LaCoO3 compound. SEM micrographs clearly revealed quite spherical particles with a mean size in the range 139–178 nm and high tendency to clustering, meanwhile EDAX analysis confirmed the corresponding chemical composition with homogeneous distribution of the constituent elements. A weak paramagnetic order is observed irrespective of F/O ratio, with slight increase of the effective magnetic moment with F/O ratio; 2.72–2.93 μB, due to the presence of more high spin states.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.