Abstract
ABSTRACT Sighter Induced Roll Magnetic Separation tests were conducted on a ferromanganese ore sample to determine the potential to significantly upgrade the Mn content and Mn:Fe ratio. The sample had a Mn:Fe ratio of 1.3 and was comprised of hematite, cryptomelane, pyrolusite, quartz, goethite and braunite. Tests at 4.7, 2.3 and 1 mm top sizes revealed better separation of Fe from Mn at the 2.3 and 1 mm top sizes. This reflected the better liberation and separation characteristics of Fe oxides at 2.3 mm and both Fe and Mn oxides at 1 mm. A test on the −2.3 + 0.6 mm size fraction improved the Mn:Fe ratio to 4.6, the Mn content to 41.5 wt% with 69.4% mass recovery and 84.2% Mn recovery. Particle magnetic susceptibility was influenced by particle microporosity, and its effect on apparent density, resulting in some Mn oxides reporting to the magnetic concentrate and Fe oxides to the tails.
Sign-in/Register to access full text options 
Free) 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a call