We demonstrate the growth and fabrication of a semipolar (101¯3¯) InGaN∕GaN green (∼525nm) light emitting diode (LED). The fabricated devices demonstrated a low turn-on voltage of 3.2V and a series resistance of 14.3Ω. Electroluminescence measurements on the semipolar LED yielded a reduced blueshifting of the peak emission wavelength with increasing drive current, compared to a reference commercial c-plane LED. On-wafer measurements yielded an approximately linear increase in output power with drive current, with measured values of 19.3 and 264μW at drive currents of 20 and 250mA, respectively. The external quantum efficiency did not decrease appreciably at high currents. Polarization anisotropy was also observed in the electroluminescence from the semipolar green LED, with the strongest emission intensity parallel to the [12¯10] direction. A polarization ratio of 0.32 was obtained at a drive current of 20mA.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.