Abstract
AbstractThe degradation mechanism in hydrogen passivated and as-fabricated poly-Si TFT's are investigated under the various electrical stress conditions. It is observed that the charge trapping in the gate dielectric is the dominant degradation mechanism in poly-Si TFT's which was stressed by the gate bias alone while the creation of defects in the poly-Si film is prevalent in gate and drain bias stressed devices. The degradation due to the gate bias stress is dramatically reduced with hydrogenation time while the degradation due to the gate and drain bias stress is increased a little. From the experimental results, it is considered that hydrogenation suppress the charge trapping at gate dielectrics as well as improve the characteristics of poly-Si TFT's.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.