Abstract
Degradation mechanism of stacked high-k gate dielectrics has been studied with metal-oxide-semiconductor capacitors having HfAlOX∕SiO2 films of various thickness combinations. A large leakage current with a peaked shape, named as the low-voltage peak current (LVPC), has been observed in the low-voltage region even in the initial current–voltage characteristics. It has been shown that a main part of LVPC is the transient current component controlled by the process of hole injection to traps in the vicinity of the HfAlOX∕SiO2 interface through the interfacial SiO2 layer. By the electrical stress, both the transient and the steady-state current components monotonically increase with time having different rates. Steady-state component has significantly larger rate than the transient component, and the same rate with the stress-induced leakage current (SILC) observed in the high-voltage region, indicating that the steady-state component of LVPC should be regarded as the SILC in the higher-voltage region extending down to the lower gate voltage region where the LVPC is observed.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.