Abstract
The purpose of this study was to investigate the degradation in performance of four major alloys of orthodontic wires, namely nickel-titanium, beta titanium, stainless steel, and cobalt-chromium-nickel, caused by hydrogen absorption during short-term immersion in an acid fluoride solutions. The hydrogen-related degradation of orthodontic wires after immersion in 2.0% acidulated phosphate fluoride solution at 37 degrees C for 60 minutes was evaluated by a tensile test, scanning electron microscope observation, and hydrogen thermal desorption analysis. Upon immersion, the tensile strengths of the nickel-titanium and beta titanium wires decreased. Particularly, the nickel-titanium wire fractured before yielding, and the fracture mode changed from ductile to brittle. The amounts of absorbed hydrogen in the nickel-titanium and beta titanium wires were 200 and 100 mass ppm, respectively. On the other hand, the tensile strengths of the stainless steel and cobalt-chromium-nickel wires were only slightly affected by immersion. The results of this study suggest that degradation in performance of orthodontic wires of titanium alloys occurs because of hydrogen absorption even after a short-term immersion in fluoride solutions.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.