Abstract
We study Cu2O/InGaN heterojunction thin films with different thicknesses of Cu2O layer as a photoanode in photoelectrochemical (PEC) water splitting cell. Results show that the bandgap energy of Cu2O/InGaN heterojunction thin films is 2.60–2.72 eV and, according to Vegard’s law, the indium content of the InGaN thin film is 22%. Electrochemical impedance spectroscopy shows the charge-transfer resistance value of about 0.4 kΩ for the optimized sample revealing enhanced charge separation and transfer at the interface. A maximum photocurrent density of 0.16 mA cm−2 at 0.5 V vs. Ag/AgCl was obtained for the Cu2O/InGaN heterojunction thin films with an overall thickness of 250 nm. The obtained value is 4.2 and 3.2 times higher than that of pure InGaN and Cu2O thin films photoanodes, respectively. We showed charge separation mechanism in the Cu2O/InGaN heterojunction photoelectrodes. According to our model, gradient energy bandgap reduce the recombination rate of photo-induced electron-hole pairs, and significantly enhance the PEC performance.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.