Crystallization and melting of poly(glycerol adipate)‐based graft copolymers with single and double crystallizable side chains

Abstract

ABSTRACTThe crystallization and melting behavior of a series of poly(glycerol adipate) (PGA) based graft copolymers with either poly(ε‐caprolactone) (PCL), poly(ethylene oxide) (PEO), or PCL‐b‐PEO diblock copolymer side chains (i.e., PGA‐g‐PCL, PGA‐g‐PEO, and PGA‐g‐(PCL‐b‐PEO)) was studied using polarized light optical microscopy (POM), differential scanning calorimetry (DSC), small‐angle X‐ray scattering (SAXS), and wide‐angle X‐ray diffraction (WAXD). These results were compared with the behavior of the corresponding linear analogs (PEO, PCL, and PCL‐b‐PEO). POM revealed that spherulitic morphology was retained after grafting. However, spherulite radius as well as radial growth rate was significantly smaller in the graft copolymers. Evaluation of isothermal crystallization kinetics by means of the Avrami theory revealed that the nucleation density was much higher in the graft copolymers. The DSC results indicated that the degree of crystallinity decreased strongly upon grafting while the melting temperatures of PGA‐g‐PCL and PGA‐g‐PEO were found to be close to the values of neat PCL and PEO, respectively. This was attributed to the absence of specific thermodynamic interactions, and, additionally, to lamella thicknesses being similar to those of the homopolymers. The latter point was confirmed by SAXS measurements. In case of PCL‐b‐PEO diblock copolymers and PGA‐g‐(PCL‐b‐PEO) graft copolymers, the crystallization behavior and thus the resulting lamellar morphology is more complex, and a suitable model was developed based on a combination of DSC, WAXD, and SAXS data. © 2013 Wiley Periodicals, Inc. J. Polym. Sci., Part B: Polym. Phys. 2013, 51, 1581–1591