Abstract
The mechanical properties of spodumene-diopside glasses ceramics with 4-12% TiO2 were investigated. The main crystalline phases precipitated were eucryptite, β-spodumene and diopside. As TiO2 content increasing, the morphology of glass ceramics transformed from coarse to fine microstructure, then to reverse. The flexural strength, elastic moduli, Vickers hardness and fracture toughness of the glass-ceramics were measured. The flexural strength of glass–ceramics containing 9%TiO2 was 198MPa, the Young’s modulus and fracture toughness were 91.3GPa and 2.3 MPa·m1/2 respectively. It was indicated that the mechanical properties were correlated with crystallization and morphology of glass ceramics
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.