Abstract
The flexural strength, elastic moduli, Vickers hardness and fracture toughness for silicate glass-ceramics (anorthite and diopside) containing tricalcium phosphate (TCP) were measured. The microstructures of the silicate glass–ceramics containing TCP were shown to consist of a complex structure of rod-like silicate and TCP crystals. The flexural strengths of glass–ceramics containing 32 wt% TCP for anorthite and 38 wt% TCP for diopside corresponding to a eutectic composition in the phase diagram were 236 and 226 MPa. The Young’s modulus and fracture toughness of the eutectic compositions were 89.4 GPa and 2.5 MPa·m1/2 for anorthite and 126 GPa and 2.3 MPa·m1/2 for diopside, respectively. The anorthite glass–ceramic containing TCP has a lower Young’s modulus in spite of a high strength as compared to other silicate glass–ceramics containing apatite or TCP.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.