Abstract
The crystal structure and microwave dielectric properties of apatite‐type LiRE9(SiO4)6O2 ceramics (RE = La, Pr, Nd, Sm, Eu, Gd, and Er) have been investigated. The densification of lithium apatites has been greatly improved with the addition of 1 wt% LiF. Selected area electron diffraction and X‐ray diffraction (XRD) Rietveld analysis confirm that these compounds belong to the P63/m (No. 176) space group with hexagonal crystal symmetry. The porosity‐corrected relative permittivity was found to decrease with decreasing ionic polarizability of RE3+ ions. Relationships between the structural parameters and microwave dielectric properties have been examined. The observed variation in the quality factor of LiRE9(SiO4)6O2 + 1 wt% LiF ceramics (RE = La, Pr, and Nd) was correlated with average cation covalency (%). The temperature coefficient of resonant frequency was found to depend on the bond valence sum of cations. LiEr9(SiO4)6O2 + 1 wt% LiF ceramics showed good microwave dielectric properties with εr = 12.8, Qu × f = 13000 GHz and τf = +17 ppm/°C. All the compositions showed low coefficient of thermal expansion with thermal conductivity in the range 1.3–2.8 W (m K)−1.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.