Abstract
Tm3+:Na2La4(WO4)7, a disordered tetragonal scheelite-type tungstate crystal, is grown by the Czochralski method. The polarized absorption, stimulated-emission and gain cross-section spectra are determined. The maximum σSE is 1.62 × 10–20 cm2 at 1788.6 nm for σ-polarization. The Judd-Ofelt parameters for Tm3+ are Ω2 = 10.321, Ω4 = 0.183 and Ω6 = 2.122 [10–20 cm2]. The radiative lifetime of the 3F4 state is 1.63 ms. Raman spectroscopy reveals a maximum phonon energy of 923 cm−1. Laser operation under diode-pumping is achieved with both a-cut and c-cut Tm:Na2La4(WO4)7 crystals, reaching a maximum output power for the a-cut of 715 mW at ~ 1937 nm with a slope efficiency of 34%. Microchip laser operation using the c-cut crystal yields a slope efficiency of 41%. The Tm:Na2La4(WO4)7 crystal is promising for mode-locked lasers due to its broadband emission.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.