Abstract
We report on the crystal growth, structure, room- and low-temperature (6K) absorption and emission spectroscopy of a 3at% Yb3+-doped trigonal ordered langasite-type silicate crystal, Ca3NbGa3Si2O14 (Yb: CNGS). The Rietveld refinement data are presented. Absorption, stimulated-emission and gain cross-sections are determined for the Yb3+ ion in CNGS for π and σ polarizations. The maximum stimulated emission cross-section amounts to σSE = 0.97 × 10−20cm−2 at 1014nm (σ-polarization). The Stark splitting of the Yb3+ multiplets is resolved. Microchip laser operation is obtained with both a-cut and c-cut 3at% Yb: CNGS samples under end-pumping at 976nm by a Volume Bragg Grating-stabilized diode laser. For the latter cut, the maximum output power reaches 7.61W at 1048–1060nm with a slope efficiency of 59%. By varying the output coupling, multi-watt emission over a 50nm-broad spectral range is achieved.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.