Crystal Growth, Characterization, and Properties of Nonlinear Optical Crystals of LixAg1-xGaSe2 for Mid-Infrared Applications.

Abstract

LixAg1-xGaSe2 is a new series of solid solution crystals that has a large nonlinear optical (NLO) coefficient and laser-induced damage threshold (LIDT). It has great application prospects in mid-infrared laser frequency conversion. In this work, LixAg1-xGaSe2 (x = 0, 0.2, 0.4, 0.5, 0.6, 0.8, and 1) crystals (Φ 16 mm × 40 mm) were grown by the improved Bridgeman method in a four-zone furnace. It is found that the LixAg1-xGaSe2 (x = 0.2-0.8) crystals keep the same tetragonal symmetry with AgGaSe2 and the melting and solidification temperature increase with the Li content. Because the as-grown crystals are almost opaque in the visible-NIR range, an annealing experiment is necessary. After annealing, the transmittance is improved significantly, which can meet the application requirements. The band gap is changed by annealing atmosphere; for instance, the band gap of Li0.6Ag0.4GaSe2 annealed in a LiGaSe2 powder atmosphere increases from 2.35 to 2.56 eV, while the band gap of LiGaSe2 annealed in vacuum decreases from 3.39 to 3.01 eV. Finally, the LixAg1-xGaSe2 shows an extreme SHG response, especially Li0.8Ag0.2GaSe2, which has about five times that of LiGaSe2, proving the promising NLO properties.