Abstract
CrN/Cr multilayer coating is prepared on 316L stainless steel as bipolar plates for proton exchange membrane fuel cell (PEMFC) by pulsed bias arc ion plating (PBAIP). Interfacial conductivity of the bipolar plate with CrN/Cr multilayer is improved obviously, presenting an interfacial contact resistance (ICR) of 8.4 mΩ cm −2 under 1.4 MPa. The results tested by potentiodynamic and potentiostatic measures in simulated PEMFC environments show that the bipolar plate with CrN/Cr multilayer has good anticorrosion performance. The corrosion current density of the bipolar plate with CrN/Cr multilayer is approximately 10 −8.0 A cm −2 at 0.6 V (vs. SCE) in a 0.5 M H 2SO 4 + 5 ppm F − solution at 70 °C with pressured air purging. The results of SEM and ICR before and after corrosion tests indicate that the bipolar plate with CrN/Cr multilayer is considerably stable electrochemically. The bipolar plate with CrN/Cr multilayer combined the prominent interfacial conductivity and the excellent corrosion resistance, showing great potential of application in PEMFC.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.