Abstract
Magnetization hysteresis loops of Cu/MgB 2, Nb/MgB 2, Cu/Nb/MgB 2 and Fe/Cu/MgB 2 wires in parallel magnetic fields of up to 5 T were studied in the temperature range from 5 to 35 K. All Nb-clad samples exhibited a thermomagnetic instability (TMI) in the form of magnetization jumps. In a thick wire (about 2 mm in core diameter), the TMI persisted up to the unexpectedly high temperature of 32 K. Thin wires showed low TMI which vanished at T > 10 K. Cu/MgB 2 wires which did not contain a Nb barrier, showed no signs of TMI. The TMI in thin wires exhibited good reproducibility and stability in the jump pattern (JP) (jump amplitudes and positions), while thick wires showed the worst time stability. We found that moderate flat rolling of the round unstable Cu/Nb/MgB 2 wire resulted in negligible TMI at 5 K in the processed flat tape. The TMI amplitudes of studied samples correlated with the adiabatic stability parameter, β −1.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.