Creep strength and microstructure of a modified P911-type steel weld joint

Abstract

The creep strength and microstructure of the weld joint of the modified P911-type steel has been studied. The creep rupture time of the welded joint at 650° of 1375 h is close to that of the base metal. The heat affected zone-is found to be the weakest area due to the increased size and relatively high coarsening rate of precipitates. The increased boron content in the weld steel effectively stabilizes the M23(C,B)6 particles and is beneficial for the creep strength of the weld joint in the fusion zone.