Abstract
Creep rupture tests on Incoloy-800H and Hastelloy-X have been carried out in a simulated steamcycle high-temperature gas-cooled reactor helium environment containing a high level of moisture. For the maximum test time of 16 000 h, the creep rupture behavior of Incoloy-800H in the helium environment was not significantly different from that in air. Hastelloy-X showed a slightly lower rupture life in helium in comparison with standard air tests. Surface cracks initiated at the grain boundaries penetrating surface and cavities formed at the grain boundary triple points have been identified as major fracture mechanisms in both environments. Oxidation was the only gas/metal interaction observed in the helium environment.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.