Abstract
Creep rupture behavior of Grade 91 heat-resistant steel used for steam cooler under uniaxial and multiaxial state of stress was investigated. Creep tests were conducted at the temperature of 923K under the stress 125MPa. The notch root radii (r) of doubled circumferentially U-notched specimens were 0.6 and 6 mm. The creep rupture life of Grade 91 steel was found to increase with the increasing of notch acuity ratio. The creep rupture mechanism was investigated based on the SEM fractography analysis.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: IOP Conference Series: Materials Science and Engineering
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.