Abstract
The authors report on the tensile and creep deformation of a series of high-lead solders with 0 to 10% tin, over a temperature range of 0 degrees C to 10 degrees C. In these alloys, the yield strength is strongly influenced by the precipitation of the tin phase, which depends on temperature and tin content. The creep rupture behavior follows the Monkman-Grant relationship. The results are generally consistent with a power-low creep mechanism, controlled by dislocation-core diffusion. There is a clear trend to greater creep resistance (lower creep rate at a given stress and temperature) for alloys of higher tin concentration. It is concluded that the mechanical behavior during thermal cycling tests may depend on cycle frequency and temperature range in a manner determined by the evolution of the precipitate microstructure.< <ETX xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">></ETX>
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: IEEE Transactions on Components, Hybrids, and Manufacturing Technology
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.