Abstract
Abstract— The development of fatigue damage in Co45Ni specimens during push—pull and reversed torsion tests, performed inside a scanning electron microscope, was observed and the different stress states compared. It appeared that transgranular crack initiation and development is delayed and intergranular crack initiation promoted under torsional loading. This was explained in terms of reduced surface distortion at the emergence of persistent slip bands (PSBs) and smaller compatibility stresses at the PSB‐matrix interfaces. The influence of the mechanical strength of grain boundaries on the difference between tensile and torsional fatigue lives is discussed.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: Fatigue & Fracture of Engineering Materials & Structures
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.