Cost effective synthesis of sulfur and nitrogen co-doped graphene aerogel and application in binder free supercapacitor

Abstract

Incorporating heteroatoms into graphene lattice results in enhanced electrical conductivity and electrochemically active sites and has significant importance in developing high-performance supercapacitors. In this study, sulfur and nitrogen co-doped graphene aerogel is synthesized via hydrothermal technique followed by a simple but effective freeze-thawing and ambient pressure drying process (referred to as SN-GA). The process requires low-cost raw materials and cost-effective equipment without the utilization of any special instrument that operates at ultra-low temperatures, under high pressure, or vacuum environment. Ammonium sulfate [(NH4)2SO4] and ethylenediamine are used as a source of sulfur and nitrogen and as a reducing agent. (NH4)2SO4 with different molarities (0, 12, 24, and 36 mM) are used to synthesize four different aerogel samples marked as GA, SN-GA1, SN-GA2, and SN-GA3. The electrode is prepared using an SN-GA2 sample, exhibiting an outstanding specific capacitance of 244 F g−1 at an applied current density of 1 A g−1 with almost 98.5% Coulomb efficiency. Furthermore, based on the SN-GA2 sample, the symmetrical supercapacitor is fabricated, displaying an energy density of 18.14 Wh kg−1 at a power density of 498.4 W kg−1. Hence, SN-GA2 renders a promising material for supercapacitor applications.